The mechanical properties of semi-crystalline polymers depend extremely on their
morphology, which is dependent on the crystallization during processing. The aim of
this research is to determine the effect of various nanoparticles on morphology
formation and tensile mechanical properties of polypropylene under conditions
relevant in polymer processing and to contribute ultimately to the understanding of
this influence.
Based on the thermal analyses of samples during fast cooling, it is found that the
presence of nanoparticle enhances the overall crystallization process of PP. The results
suggest that an increase of the nucleation density/rate is a dominant process that
controls the crystallization process of PP in this work, which can help to reduce the
cycle time in the injection process. Moreover, the analysis of melting behaviors
obtained after each undercooling reveals that crystal perfection increases significantly
with the incorporation of TiO2 nanoparticles, while it is not influenced by the SiO2
nanoparticles.
This work also comprises an analysis of the influence of nanoparticles on the
microstructure of injection-molded parts. The results clearly show multi-layers along
the wall thickness. The spherulite size and the degree of crystallinity continuously
decrease from the center to the edge. Generally both the spherulite size and the degree
of crystallinity decrease with higher the SiO2 loading. In contrast, an increase in the
degree of crystallinity with an increasing TiO2 nanoparticle loading was detected.
The tensile properties exhibit a tendency to increase in the tensile strength as the core
is reached. The tensile strength decreases with the addition of nanoparticles, while the
elongation at break of nanoparticle-filled PP decreases from the skin to the core. With
increasing TiO2 loading, the elongation at break decreases.