Beitrag zur Umformtechnik gewebeverstärkter Thermoplaste

  • Fabric reinforced thermoplastic composites, suitable for the production of thin-walled, high strength structural parts, are available on the market today with various fibre/matrix combinations. However, further market penetration and series production are inhibited as long as forming technologies are not well understood. In this thesis, the potential for series production of different forming technologies is evaluated. Stamp forming is an efficient way to produce parts in very short cycle times. A limiting factor to part complexibilty is undesired wrinkle formation as a consequence of insufficient fabric shear. Fabric shear and other important deformations of impregnated fabrics were examined by means of new test devices. Evidence was found that membrane tension is the crucial factor to avoid wrinkle formation. New tool concepts and processing Windows were developed to produce fabric reinforced thermoplastic parts free of wrinkles and distortions.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Verfasserangaben:Ulf Paul Breuer
URN (Permalink):urn:nbn:de:hbz:386-kluedo-47169
Betreuer:Manfred Neitzel
Dokumentart:Dissertation
Sprache der Veröffentlichung:Deutsch
Veröffentlichungsdatum (online):07.08.2017
Datum der Erstveröffentlichung:25.06.1997
Veröffentlichende Institution:Technische Universität Kaiserslautern
Titel verleihende Institution:Technische Universität Kaiserslautern
Datum der Annahme der Abschlussarbeit:25.06.1997
Datum der Publikation (Server):08.08.2017
Seitenzahl:X, 123
Fachbereiche / Organisatorische Einheiten:Fachbereich Maschinenbau und Verfahrenstechnik
DDC-Sachgruppen:6 Technik, Medizin, angewandte Wissenschaften / 620 Ingenieurwissenschaften und Maschinenbau
Lizenz (Deutsch):Creative Commons 4.0 - Namensnennung, nicht kommerziell, keine Bearbeitung (CC BY-NC-ND 4.0)