In recent years, nanofiller-reinforced polymer composites have attracted considerable
interest from numerous researchers, since they can offer unique mechanical,
electrical, optical and thermal properties compared to the conventional polymer
composites filled with micron-sized particles or short fibers. With this background, the
main objective of the present work was to investigate the various mechanical
properties of polymer matrices filled with different inorganic rigid nanofillers, including
SiOB2B, TiOB2B, AlB2BOB3B and multi-walled carbon nanotubes (MWNT). Further, special
attention was paid to the fracture behaviours of the polymer nanocomposites. The
polymer matrices used in this work contained two types of epoxy resin (cycloaliphatic
and bisphenol-F) and two types of thermoplastic polymer (polyamide 66 and isotactic
polypropylene).
The epoxy-based nanocomposites (filled with nano-SiOB2B) were formed in situ by a
special sol-gel technique supplied by nanoresins AG. Excellent nanoparticle
dispersion was achieved even at rather high particle loading. The almost
homogeneously distributed nanoparticles can improve the elastic modulus and
fracture toughness (characterized by KBICB and GBICB) simultaneously. According to
dynamic mechanical and thermal analysis (DMTA), the nanosilica particles in epoxy
resins possessed considerable "effective volume fraction" in comparison with their
actual volume fraction, due to the presence of the interphase. Moreover, AFM and
high-resolution SEM observations also suggested that the nanosilica particles were
coated with a polymer layer and therefore a core-shell structure of particle-matrix was
expected. Furthermore, based on SEM fractography, several toughening
mechanisms were considered to be responsible for the improvement in toughness,
which included crack deflection, crack pinning/bowing and plastic deformation of
matrix induced by nanoparticles.
The PA66 or iPP-based nanocomposites were fabricated by a conventional meltextrusion
technique. Here, the nanofiller content was set constant as 1 vol.%. Relatively good particle dispersion was found, though some small aggregates still
existed. The elastic modulus of both PA66 and iPP was moderately improved after
incorporation of the nanofillers. The fracture behaviours of these materials were
characterized by an essential work fracture (EWF) approach. In the case of PA66
system, the EWF experiments were carried out over a broad temperature range
(23~120 °C). It was found that the EWF parameters exhibited high temperature
dependence. At most testing temperatures, a small amount of nanoparticles could
produce obvious toughening effects at the cost of reduction in plastic deformation of
the matrix. In light of SEM fractographs and crack opening tip (COD) analysis, the
crack blunting induced by nanoparticles might be the major source of this toughening.
The fracture behaviours of PP filled with MWNTs were investigated over a broad
temperature range (-196~80 °C) in terms of notched impact resistance. It was found
that MWNTs could enhance the notched impact resistance of PP matrix significantly
once the testing temperature was higher than the glass transition temperature (TBgB) of
neat PP. At the relevant temperature range, the longer the MWNTs, the better was
the impact resistance. SEM observation revealed three failure modes of nanotubes:
nanotube bridging, debonding/pullout and fracture. All of them would contribute to
impact toughness to a degree. Moreover, the nanotube fracture was considered as
the major failure mode. In addition, the smaller spherulites induced by the nanotubes
would also benefit toughness.