Ferromagnetism above room temperature in Mn-Si-C alloy films
- Mn-Si-C alloy films are prepared by e-beam coevaporation onto a Si substrate held at 600 °C. Ferromagnetism is observed below T = (360 +/- 5) K with SQUID magnetometry and magneto-optical Kerr effect. This is the highest Curie temperature T yet observed for a Mn-based alloy. Although the composition determined by Auger depth profiling varies appreciably for different films, their T is the same indicating that ferromagnetism is caused by an alloy of well-defined composition independent of precipitations.
Volltext Dateien herunterladen
Weitere Dienste
| Verfasser*innenangaben: | M. Gajdzik, C. Sürgers, M. Kelemen, Burkard Hillebrands, H. von Löhneysen |
|---|---|
| URN: | urn:nbn:de:hbz:386-kluedo-8917 |
| Dokumentart: | Wissenschaftlicher Artikel |
| Sprache der Veröffentlichung: | Englisch |
| Jahr der Fertigstellung: | 1999 |
| Jahr der Erstveröffentlichung: | 1999 |
| Veröffentlichende Institution: | Technische Universität Kaiserslautern |
| Datum der Publikation (Server): | 03.04.2000 |
| Freies Schlagwort / Tag: | Curie temperature; Ferromagnetism; Mn-Si-C alloy films; SQUID magnetometry; magneto-optical Kerr effect |
| Fachbereiche / Organisatorische Einheiten: | Kaiserslautern - Fachbereich Physik |
| DDC-Sachgruppen: | 5 Naturwissenschaften und Mathematik / 530 Physik |
| Lizenz (Deutsch): |  Standard gemäß KLUEDO-Leitlinien vor dem 27.05.2011 |